Product description
Fire bricks 230x114x64mm is a common refractory material with good fire resistance, corrosion resistance and mechanical strength, and is widely used in various high-temperature environment of industrial equipment, furnaces and buildings and other fields.
Fire bricks 230x114x64mm are made by clay and kaolin, and usually a certain proportion of quartz sand, bauxite, coal gangue and other auxiliary raw materials are added. The content of clay is usually between 50% and 70%, and the content of kaolin is between 10% and 30%.
Applications of fire bricks 230x114x64mm
Metallurgical industry: fire bricks 230x114x64mm can be used in iron furnaces, steel furnaces, blast furnaces, ladle, converter, electric furnaces and other metallurgical equipment lining, furnace bottom, hot air duct and other parts.
Power industry: fire bricks 230x114x64mm can be used in power station boiler, flue, desulfurization equipment, dust removal equipment, burner and other high temperature parts.
Physical and chemical index of fire bricks 230x114x64mm
|
Items |
Index |
|
||||||||
|
/ |
N-1 |
N2a |
N2b |
N-3a |
N-3b |
N-4 |
N-5 |
N-6 |
||
|
Refractoriness /℃≥ |
1750 |
1730 |
1730 |
1710 |
1710 |
1690 |
1670 |
1580 |
||
|
0.2Mpa Refractoriness under load(RUL)/℃≥ |
1400 |
1350 |
/ |
1320 |
/ |
1300 |
/ |
/ |
||
|
Reheating linear change/℃(1500℃,2h) |
1400℃,2h |
+0.1 -0.4 |
+0.1 -0.5 |
+0.2 -0.5 |
/ |
/ |
/ |
/ |
/ |
|
|
1350℃,2h |
|
|
|
+0.2 -0.5 |
+0.2 -0.5 |
+0.2 -0.5 |
+0.2 -0.5 |
|
||
|
Apparent porosity/% ≤ |
22 |
24 |
26 |
24 |
26 |
24 |
26 |
28 |
||
|
CCS/Mpa ≥ |
30 |
25 |
20 |
15 |
15 |
20 |
15 |
15 |
||
Packages:
Physical and chemical index of fire bricks 230x114x64mm
|
Items |
Index |
|
||||||||
|
/ |
N-1 |
N2a |
N2b |
N-3a |
N-3b |
N-4 |
N-5 |
N-6 |
||
|
Refractoriness /℃≥ |
1750 |
1730 |
1730 |
1710 |
1710 |
1690 |
1670 |
1580 |
||
|
0.2Mpa Refractoriness under load(RUL)/℃≥ |
1400 |
1350 |
/ |
1320 |
/ |
1300 |
/ |
/ |
||
|
Reheating linear change/℃(1500℃,2h) |
1400℃,2h |
+0.1 -0.4 |
+0.1 -0.5 |
+0.2 -0.5 |
/ |
/ |
/ |
/ |
/ |
|
|
1350℃,2h |
|
|
|
+0.2 -0.5 |
+0.2 -0.5 |
+0.2 -0.5 |
+0.2 -0.5 |
|
||
|
Apparent porosity/% ≤ |
22 |
24 |
26 |
24 |
26 |
24 |
26 |
28 |
||
|
CCS/Mpa ≥ |
30 |
25 |
20 |
15 |
15 |
20 |
15 |
15 |
||