Product description
Heat resistant fire bricks have good wear resistance: clay firebrick has high hardness and density, and its surface is not easy to wear, so it can maintain surface finish and mechanical strength at high temperatures for a long time.
Applications of heat resistant fire bricks
Chemical industry: heat resistant fire bricks can be used in oil refining, fertilizer, ethylene and other chemical equipment lining, reactors, pipelines, heating furnaces and other parts.
Power industry: heat resistant fire bricks can be used in power station boiler, flue, desulfurization equipment, dust removal equipment, burner and other high temperature parts.
Other industries: heat resistant fire bricks can also be used in glass, ceramics, petrochemical, mining, machinery manufacturing and other fields.
Physical and chemical index of heat resistant fire bricks
|
Items |
Index |
|
||||||||
|
/ |
N-1 |
N2a |
N2b |
N-3a |
N-3b |
N-4 |
N-5 |
N-6 |
||
|
Refractoriness /℃≥ |
1750 |
1730 |
1730 |
1710 |
1710 |
1690 |
1670 |
1580 |
||
|
0.2Mpa Refractoriness under load(RUL)/℃≥ |
1400 |
1350 |
/ |
1320 |
/ |
1300 |
/ |
/ |
||
|
Reheating linear change/℃(1500℃,2h) |
1400℃,2h |
+0.1 -0.4 |
+0.1 -0.5 |
+0.2 -0.5 |
/ |
/ |
/ |
/ |
/ |
|
|
1350℃,2h |
|
|
|
+0.2 -0.5 |
+0.2 -0.5 |
+0.2 -0.5 |
+0.2 -0.5 |
|
||
|
Apparent porosity/% ≤ |
22 |
24 |
26 |
24 |
26 |
24 |
26 |
28 |
||
|
CCS/Mpa ≥ |
30 |
25 |
20 |
15 |
15 |
20 |
15 |
15 |
||
Packages:
Physical and chemical index of heat resistant fire bricks
|
Items |
Index |
|
||||||||
|
/ |
N-1 |
N2a |
N2b |
N-3a |
N-3b |
N-4 |
N-5 |
N-6 |
||
|
Refractoriness /℃≥ |
1750 |
1730 |
1730 |
1710 |
1710 |
1690 |
1670 |
1580 |
||
|
0.2Mpa Refractoriness under load(RUL)/℃≥ |
1400 |
1350 |
/ |
1320 |
/ |
1300 |
/ |
/ |
||
|
Reheating linear change/℃(1500℃,2h) |
1400℃,2h |
+0.1 -0.4 |
+0.1 -0.5 |
+0.2 -0.5 |
/ |
/ |
/ |
/ |
/ |
|
|
1350℃,2h |
|
|
|
+0.2 -0.5 |
+0.2 -0.5 |
+0.2 -0.5 |
+0.2 -0.5 |
|
||
|
Apparent porosity/% ≤ |
22 |
24 |
26 |
24 |
26 |
24 |
26 |
28 |
||
|
CCS/Mpa ≥ |
30 |
25 |
20 |
15 |
15 |
20 |
15 |
15 |
||