Product description
The composition of refractory brick for fireplace is aluminum, the production technology is to add high alumina particles in different proportions to high alumina powder, which is formed under high pressure and sintered at high temperature. So CH Refractories dense refractory bricks have high strength and good thermal shock stability.
Advantages of superior clay firebrick
When the refractory brick for fireplace is calcined, its high-density step has long been from the outer surface of the exposed heated vapor state, if before this period, the carbon and other materials remaining in the body of the body are completely burned, after 1200℃, co2 is very difficult to insert into the body, unnecessary residual carbon and so on prevent the calcination of raw materials during firing, and will form a porous structure in the center of the product. The unqualified rate increased. Then the necessary temperature raising speed and trolley rail system should be maintained in the pre-subtropical zone. .
Physical and chemical index of refractory brick for fireplace
|
Items |
Index |
|||
|
/ |
CH-LZ75 |
CH-LZ65 |
CH-LZ55 |
CH-LZ48 |
|
Al2O3%≥ |
75 |
65 |
55 |
48+ |
|
CCS/Mpa ≥ |
54 |
49 |
44 |
40 |
|
Apparent porosity/% ≤ |
23 |
23 |
22 |
22 |
|
Refractoriness under load /℃ ≥ |
1520 |
1500 |
1470 |
1420 |
|
Reheating linear change(1500℃,2h) |
+0.1 -0.4 |
+0.1 -0.4 |
+0.1 -0.4 |
+0.1 -0.4(1450℃.2h) |
|
Refractoriness/℃≥ |
1790 |
1790 |
1770 |
1750 |
Packages:
Physical and chemical index of refractory brick for fireplace
|
Items |
Index |
|||
|
/ |
CH-LZ75 |
CH-LZ65 |
CH-LZ55 |
CH-LZ48 |
|
Al2O3%≥ |
75 |
65 |
55 |
48+ |
|
CCS/Mpa ≥ |
54 |
49 |
44 |
40 |
|
Apparent porosity/% ≤ |
23 |
23 |
22 |
22 |
|
Refractoriness under load /℃ ≥ |
1520 |
1500 |
1470 |
1420 |
|
Reheating linear change(1500℃,2h) |
+0.1 -0.4 |
+0.1 -0.4 |
+0.1 -0.4 |
+0.1 -0.4(1450℃.2h) |
|
Refractoriness/℃≥ |
1790 |
1790 |
1770 |
1750 |