Product description
Refractory concrete bricks for fireplace have different production process, if add a certain proportion of phosphoric acid and sintering at low temperature, phosphate bricks can be produced. By adding a certain proportion of silicon carbide, high-temperature sintering can produce silicon molybdenum bricks or silicon carbide bricks. Adding Andalusite and sillimanite of different proportions can produce low creep high alumina bricks.
Application of refractory concrete bricks
Refractory concrete bricks mainly used for laying blast furnace, hot blast furnace, electric furnace top, blast furnace, reverberatory furnace, rotary kiln lining. In addition, high alumina brick is also widely used as open hearth regenerative lattice brick, plug head for pouring system, water brick and so on. However, the price of high aluminum bricks is higher than that of clay bricks, so there is no need to use high aluminum bricks where clay bricks can meet the requirements.
Physical and chemical index of refractory concrete bricks
|
Items |
Index |
|||
|
/ |
CH-LZ75 |
CH-LZ65 |
CH-LZ55 |
CH-LZ48 |
|
Al2O3%≥ |
75 |
65 |
55 |
48+ |
|
CCS/Mpa ≥ |
54 |
49 |
44 |
40 |
|
Apparent porosity/% ≤ |
23 |
23 |
22 |
22 |
|
Refractoriness under load /℃ ≥ |
1520 |
1500 |
1470 |
1420 |
|
Reheating linear change(1500℃,2h) |
+0.1 -0.4 |
+0.1 -0.4 |
+0.1 -0.4 |
+0.1 -0.4(1450℃.2h) |
|
Refractoriness/℃≥ |
1790 |
1790 |
1770 |
1750 |
Packages:
Physical and chemical index of refractory concrete bricks
|
Items |
Index |
|||
|
/ |
CH-LZ75 |
CH-LZ65 |
CH-LZ55 |
CH-LZ48 |
|
Al2O3%≥ |
75 |
65 |
55 |
48+ |
|
CCS/Mpa ≥ |
54 |
49 |
44 |
40 |
|
Apparent porosity/% ≤ |
23 |
23 |
22 |
22 |
|
Refractoriness under load /℃ ≥ |
1520 |
1500 |
1470 |
1420 |
|
Reheating linear change(1500℃,2h) |
+0.1 -0.4 |
+0.1 -0.4 |
+0.1 -0.4 |
+0.1 -0.4(1450℃.2h) |
|
Refractoriness/℃≥ |
1790 |
1790 |
1770 |
1750 |