Product description
Cement with a refractory degree of not less than 1580°C is 3000f refractory cement. 3000f refractory cement is also called aluminate cement.
3000f refractory cement is made of bauxite and limestone as raw materials. It is made by calcining calcium aluminate as the main component and oxidized. Clinker with an aluminum content of about 50% is ground into a hydraulic cementitious material.
3000f refractory cement can be divided into aluminate refractory cement, low calcium aluminate refractory cement, calcium magnesium aluminate cement and Baiyun according to different compositions. Stone refractory cement, etc.
CH Refractries manufactured refractory cement with very stable performance and has been exported to many countires. When exporting we packaged refractory cement with more than 4 layers bags to protect cement from moisture when shipping on the sea.
Chemical and physical index of 3000f refractory cement
|
Brand |
CA50- A600 |
CA50-A700 |
CA50-A900 |
CA-70 |
|
|
Chemical Composition (%) |
Al2O3 |
≥50 |
≥51 |
≥53.5 |
68.5-70.5 |
|
SiO2 |
≤7.8 |
≤7.5 |
≤5.5 |
≤0.5 |
|
|
Fe2O3 |
≤2.5 |
≤2.5 |
≤2.5 |
≤0.2 |
|
|
CaO |
/ |
/ |
/ |
28.5-30.5 |
|
|
MgO |
/ |
/ |
/ |
≤0.4 |
|
|
R2O |
≤0.4 |
≤0.4 |
≤0.4 |
≤0.4 |
|
|
S |
≤0.1 |
≤0.1 |
≤0.1 |
/ |
|
|
Cl |
≤0.1 |
≤0.1 |
≤0.1 |
/ |
|
|
325 mesh residue on sieve(%) |
≤15 |
≤12 |
≤8 |
/ |
|
|
d50(μm) |
/ |
/ |
/ |
11-14 |
|
|
-45μm(%) |
/ |
/ |
/ |
≤8.0 |
|
|
Specific Surface (m2/kg) |
≥300 |
≥320 |
≥350 |
/ |
|
|
Setting time(h:min) |
Initial setting (min) |
≥45 |
≥60 |
≥90 |
120-180 |
|
Final Setting (min) |
≤6 |
≤6 |
≤6 |
150-240 |
|
|
Cold Modulus of Rupture (MPa) |
24 hour |
≥6 |
≥6.5 |
≥8 |
7.5-10 |
|
72 hour |
≥7 |
≥7.5 |
≥10 |
10-12 |
|
|
Cold Crushing Strength (Mpa) |
24hour |
≥45 |
≥55 |
≥72 |
40-50 |
|
72hour |
≥55 |
≥65 |
≥82 |
45-55 |
|
Packages:
CH Refractories was founded in 1984, have advanced process equipment and raw material preparation system, and a full set of refractories conventional testing equipment, can ensure the quality before sending to customers.
01
High Quality
CH Refractories supplying refractory cement is famous brand and listed the top three in China
02
Advanced Equipment
Our production line is hundred automatical and can guarantee extremely quality
03
Professional Team
We have 30 years manufacturing experience and 10 years exporting experience
04
Custom Service
There is 7*24h service
FAQ
Q: How can I get price at soonest?
Q: Can I get sample for testing?
Q: What is MOQ of your product?
Q: How can you guarantee your products quality
Q: Which countries you mainly exporting to?
Q: How long is the production time?
Q: What payment term you can accept?
Q: Can you do OEM? Or customized packages?
Q: Can I visit your factory?
Chemical and physical index of 3000f refractory cement
|
Brand |
CA50- A600 |
CA50-A700 |
CA50-A900 |
CA-70 |
|
|
Chemical Composition (%) |
Al2O3 |
≥50 |
≥51 |
≥53.5 |
68.5-70.5 |
|
SiO2 |
≤7.8 |
≤7.5 |
≤5.5 |
≤0.5 |
|
|
Fe2O3 |
≤2.5 |
≤2.5 |
≤2.5 |
≤0.2 |
|
|
CaO |
/ |
/ |
/ |
28.5-30.5 |
|
|
MgO |
/ |
/ |
/ |
≤0.4 |
|
|
R2O |
≤0.4 |
≤0.4 |
≤0.4 |
≤0.4 |
|
|
S |
≤0.1 |
≤0.1 |
≤0.1 |
/ |
|
|
Cl |
≤0.1 |
≤0.1 |
≤0.1 |
/ |
|
|
325 mesh residue on sieve(%) |
≤15 |
≤12 |
≤8 |
/ |
|
|
d50(μm) |
/ |
/ |
/ |
11-14 |
|
|
-45μm(%) |
/ |
/ |
/ |
≤8.0 |
|
|
Specific Surface (m2/kg) |
≥300 |
≥320 |
≥350 |
/ |
|
|
Setting time(h:min) |
Initial setting (min) |
≥45 |
≥60 |
≥90 |
120-180 |
|
Final Setting (min) |
≤6 |
≤6 |
≤6 |
150-240 |
|
|
Cold Modulus of Rupture (MPa) |
24 hour |
≥6 |
≥6.5 |
≥8 |
7.5-10 |
|
72 hour |
≥7 |
≥7.5 |
≥10 |
10-12 |
|
|
Cold Crushing Strength (Mpa) |
24hour |
≥45 |
≥55 |
≥72 |
40-50 |
|
72hour |
≥55 |
≥65 |
≥82 |
45-55 |
|