Product description
Refractory cement 25kg using high-quality bauxite and high-quality lime as raw materials, they are mixed into an appropriate amount of raw material according to a certain proportion. After sintering, the clinker with aluminate as the main component is obtained, and then ground into fine powder to make fire-resistant water Hard cementitious material, called refractory cement. The refractory degree of refractory cement is not less than 1580 degrees Celsius.
Refractory cement is a hydraulic cementitious material made from finely ground bauxite and limestone as its main mineral components, codenamed CA.
The Al2O3 content of CA50 refractory cement is not less than 50%, the specific surface area is not less than 320 (m²/Kg), the initial setting time is generally 50 to 120 minutes, and the final setting time is 90 to 180 minutes. The strength should be greater than 50MPa after 3 days of testing.
The performance of CA50 refractory cement has the characteristics of concentrated heat release, stable performance, and fast setting and hardening speed.
Chemical and physical index of refractory cement 25kg
|
Brand |
CA50- A600 |
CA50-A700 |
CA50-A900 |
CA-70 |
|
|
Chemical Composition (%) |
Al2O3 |
≥50 |
≥51 |
≥53.5 |
68.5-70.5 |
|
SiO2 |
≤7.8 |
≤7.5 |
≤5.5 |
≤0.5 |
|
|
Fe2O3 |
≤2.5 |
≤2.5 |
≤2.5 |
≤0.2 |
|
|
CaO |
/ |
/ |
/ |
28.5-30.5 |
|
|
MgO |
/ |
/ |
/ |
≤0.4 |
|
|
R2O |
≤0.4 |
≤0.4 |
≤0.4 |
≤0.4 |
|
|
S |
≤0.1 |
≤0.1 |
≤0.1 |
/ |
|
|
Cl |
≤0.1 |
≤0.1 |
≤0.1 |
/ |
|
|
325 mesh residue on sieve(%) |
≤15 |
≤12 |
≤8 |
/ |
|
|
d50(μm) |
/ |
/ |
/ |
11-14 |
|
|
-45μm(%) |
/ |
/ |
/ |
≤8.0 |
|
|
Specific Surface (m2/kg) |
≥300 |
≥320 |
≥350 |
/ |
|
|
Setting time(h:min) |
Initial setting (min) |
≥45 |
≥60 |
≥90 |
120-180 |
|
Final Setting (min) |
≤6 |
≤6 |
≤6 |
150-240 |
|
|
Cold Modulus of Rupture (MPa) |
24 hour |
≥6 |
≥6.5 |
≥8 |
7.5-10 |
|
72 hour |
≥7 |
≥7.5 |
≥10 |
10-12 |
|
|
Cold Crushing Strength (Mpa) |
24hour |
≥45 |
≥55 |
≥72 |
40-50 |
|
72hour |
≥55 |
≥65 |
≥82 |
45-55 |
|
Packages:
Chemical and physical index of refractory cement 25kg
|
Brand |
CA50- A600 |
CA50-A700 |
CA50-A900 |
CA-70 |
|
|
Chemical Composition (%) |
Al2O3 |
≥50 |
≥51 |
≥53.5 |
68.5-70.5 |
|
SiO2 |
≤7.8 |
≤7.5 |
≤5.5 |
≤0.5 |
|
|
Fe2O3 |
≤2.5 |
≤2.5 |
≤2.5 |
≤0.2 |
|
|
CaO |
/ |
/ |
/ |
28.5-30.5 |
|
|
MgO |
/ |
/ |
/ |
≤0.4 |
|
|
R2O |
≤0.4 |
≤0.4 |
≤0.4 |
≤0.4 |
|
|
S |
≤0.1 |
≤0.1 |
≤0.1 |
/ |
|
|
Cl |
≤0.1 |
≤0.1 |
≤0.1 |
/ |
|
|
325 mesh residue on sieve(%) |
≤15 |
≤12 |
≤8 |
/ |
|
|
d50(μm) |
/ |
/ |
/ |
11-14 |
|
|
-45μm(%) |
/ |
/ |
/ |
≤8.0 |
|
|
Specific Surface (m2/kg) |
≥300 |
≥320 |
≥350 |
/ |
|
|
Setting time(h:min) |
Initial setting (min) |
≥45 |
≥60 |
≥90 |
120-180 |
|
Final Setting (min) |
≤6 |
≤6 |
≤6 |
150-240 |
|
|
Cold Modulus of Rupture (MPa) |
24 hour |
≥6 |
≥6.5 |
≥8 |
7.5-10 |
|
72 hour |
≥7 |
≥7.5 |
≥10 |
10-12 |
|
|
Cold Crushing Strength (Mpa) |
24hour |
≥45 |
≥55 |
≥72 |
40-50 |
|
72hour |
≥55 |
≥65 |
≥82 |
45-55 |
|