Product description
The AZS non-castable material is a kind of refractory material made from recycled AZS bricks through cleaning, grinding, crushing, screening and impurity removal. It can be reused for the production of refractory bricks and casting materials. The cost is much lower than that of AZS grout and aggregates, but it retains the chemical composition of AZS bricks. It is a highly cost-effective alternative to high-end refractory aggregates.
Application of fused cast azs block powder
The AZS non-castable refractory materials produced by our company can be customized with different particle sizes. They can be widely used in the production of refractory materials, building floor tiles, and various high-temperature resistant environments.
Physical and chemical index of fused cast azs block powder
|
Brand |
AZS33-Y |
AZS36-Y |
AZS41-Y |
|
|
Chemical compostion％ |
Zr02 |
32.00-36.00 |
35.00-40.00 |
40.00-44.00 |
|
Si02 |
≤16.00 |
≤14.00 |
≤13.00 |
|
|
Na20 |
≤1.45 |
≤1.45 |
≤1.30 |
|
|
Fe2O3+TiO2+CaO+MgO+Na2O+K2O |
≤2.00 |
≤2.00 |
≤2.00 |
|
|
Fe2O3+TiO2 |
≤0.30 |
≤0.30 |
≤0.30 |
|
|
Bulk density g/cm3 |
≥3. 75 |
≥3. 80 |
≥3. 95 |
|
|
Apparent porosity |
≤1.5% |
≤1.0% |
≤1.0% |
|
|
Staticanti-corrosion rate of glass liquid(normal soda-lime glassmeglass,1500℃x36h) |
≤1.50mm/24h |
≤1.40mm/24h |
≤1.30mm/24h |
|
|
Exudation temperature of vitreous phase |
≥1400℃ |
≥1400℃ |
≥1400℃ |
|
|
Bubble precipitation rate (normal soda lime glassmeglass,1300℃x10h)) |
≤2.0% |
≤1.5% |
≤1.0% |
|
|
Vitreous phase seepage amount(1500°Cx4h) |
≤2.0% |
≤3.0% |
≤3.0% |
|
|
Volume weight |
PT,QX |
≥3. 45g/cm3 |
≥3. 45g/cm3 |
≥3. 55g/cm3 |
|
ZWS |
≥3. 60g/cm3 |
≥3. 70g/cm3 |
≥3. 85g/cm3 |
|
|
WS |
≥3. 70g/cm3 |
≥3. 80g/cm3 |
≥3. 95g/cm3 |
|
Packages
CH Refractories have advanced refractory products manufacturing process equipment and raw material preparation system, batching using electronic batching car, mixing using 750 forced mixer, molding equipment: 2 sets 1000 tons of brick press , 4 sets 630 tons of brick press, 14 sets 400 tons of brick press , 22 sets 315 tons of brick press, 2 sets 160 tons of brick press ,8 sets 60 tons of brick press . Also have a full set of refractories conventional testing equipment, can ensure the quality before sending products to customers.
Proven Experience
CH Refractories was founded in 1984 with decades experience in producing refractory products
Professional Team
More than 30 years manufacturing experience and 10 years exporting experience
qualified staff
ISO 9001/SGS testing report
FAQ
Q: How can I get price at soonest?
Q: Can I get sample for testing?
Q: What is MOQ of your product?
Q: How can you guarantee your products quality
Q: Which countries you mainly exporting to?
Q: How long is the production time?
Q: What payment term you can accept?
Q: Can you do OEM? Or customized packages?
Q: Can I visit your factory?
Physical and chemical index of fused cast azs block
|
Brand |
AZS33-Y |
AZS36-Y |
AZS41-Y |
|
|
Chemical compostion％ |
Zr02 |
32.00-36.00 |
35.00-40.00 |
40.00-44.00 |
|
Si02 |
≤16.00 |
≤14.00 |
≤13.00 |
|
|
Na20 |
≤1.45 |
≤1.45 |
≤1.30 |
|
|
Fe2O3+TiO2+CaO+MgO+Na2O+K2O |
≤2.00 |
≤2.00 |
≤2.00 |
|
|
Fe2O3+TiO2 |
≤0.30 |
≤0.30 |
≤0.30 |
|
|
Bulk density g/cm3 |
≥3. 75 |
≥3. 80 |
≥3. 95 |
|
|
Apparent porosity |
≤1.5% |
≤1.0% |
≤1.0% |
|
|
Staticanti-corrosion rate of glass liquid(normal soda-lime glassmeglass,1500℃x36h) |
≤1.50mm/24h |
≤1.40mm/24h |
≤1.30mm/24h |
|
|
Exudation temperature of vitreous phase |
≥1400℃ |
≥1400℃ |
≥1400℃ |
|
|
Bubble precipitation rate (normal soda lime glassmeglass,1300℃x10h)) |
≤2.0% |
≤1.5% |
≤1.0% |
|
|
Vitreous phase seepage amount(1500°Cx4h) |
≤2.0% |
≤3.0% |
≤3.0% |
|
|
Volume weight |
PT,QX |
≥3. 45g/cm3 |
≥3. 45g/cm3 |
≥3. 55g/cm3 |
|
ZWS |
≥3. 60g/cm3 |
≥3. 70g/cm3 |
≥3. 85g/cm3 |
|
|
WS |
≥3. 70g/cm3 |
≥3. 80g/cm3 |
≥3. 95g/cm3 |
|